| 更新时间：2012.03.19 浏览次数： | ||||||
| 弹簧回火收缩量相关参数的数据汇总 表一 V1 V2 V3 V4 V5 V6 V7 V8 V9 序号 规格(d) 材质 △D（收缩量） C（旋绕比） D（中径） T（温度） C*D*T C*D*T/1000000 1 4.50 55CrSi 0.25 6.83 30.75 420 88209.45 0.08820945 2 4.00 55CrSi 0.26 8.385 33.54 420 118117.818 0.118117818 3 4.00 55CrSi 0.20 6.375 25.50 420 68276.25 0.06827625 4 3.10 55CrSi 0.16 7.997 24.79 420 83263.1646 0.08326316 5 4.00 55CrSi 0.20 6.35 25.40 420 67741.8 0.0677418 6 4.00 55CrSi 0.30 6.925 27.70 420 80565.45 0.08056545 7 3.10 SWOSC-V 0.15 6.452 20.00 420 54196.8 0.0541968 8 4.00 SWOSC-V 0.20 6.225 24.90 420 65101.05 0.06510105 9 3.20 SWOSC-V 0.10 6.594 21.10 420 58436.028 0.058436028 10 3.00 55CrSi 0.20 6.633 19.90 420 55438.614 0.055438614 11 4.00 55CrSi 0.20 6.425 25.70 420 69351.45 0.06935145 12 4.00 55CrSi 0.20 6.225 24.90 420 65101.05 0.06510105 13 3.10 55CrSi 0.25 6.726 20.85 420 58899.582 0.058899582 14 4.20 OTEVA70 0.10 5.76 24.20 420 58564.968 0.058564968 15 3.60 OTEVA70 0.10 7 25.20 420 74088 0.074088 16 4.75 55CrSi 0.20 6.06 28.80 420 73301.76 0.07330176 17 4.90 55CrSi 0.20 5.9 28.91 420 71638.98 0.07163898 18 4.50 55CrSi 0.20 7.89 35.50 420 117639.9 0.1176399 19 3.00 50CrV 0.11 8.00 24.00 360 69120 0.06912 20 3.20 55CrSi 0.20 6.063 19.40 420 49401.324 0.049401324 21 2.50 SWOCV-V 0.20 8.8 22.00 420 81312 0.081312 22 4.25 SWOCV-V 0.25 7.224 30.70 420 93146.256 0.093146256 23 11.8 55CrSi 1.1 10.042 118.5 420 499790.34 0.49979034 24 13 55CrSi 1.1 9.023 117.3 420 444527.118 0.444527118 25 10.5 55CrSi 1 8.762 92 420 338563.68 0.33856368 26 10.4 55CrSi 0.4 6.654 69.2 420 193391.856 0.193391856 27 12.7 55CrSi 2.3 10.866 138 420 629793.36 0.62979336 28 11.5 55CrSi 0.6 10.374 119.3 410 507423.462 0.507423462 29 10.5 55CrSi 1.5 9.476 99.5 420 396002.04 0.39600204 30 10.2 55CrSi 0.75 9.049 92.3 395 329912.9665 0.329912967 31 11 55CrSi 1.5 9 99 420 374220 0.37422 32 10.7 55CrSi 1.5 9.28 99.3 420 387031.68 0.38703168 33 10 55CrSi 0.75 9.25 92.5 420 359362.5 0.3593625 34 9.5 SWOSC-B 0.5 10.526 100 395 415777 0.415777 35 13.6 SWOSC-B 1.55 7.985 108.6 420 364211.82 0.36421182 36 14 SWOSC-B 1 7.786 109 420 356443.08 0.35644308 37 10.5 SWOSC-B 1.2 8.762 92.5 400 324194 0.324194 38 14 SWOSC-B 2 11.143 156 420 730089.36 0.73008936 39 12.5 SWOSC-B 2 8.56 107 420 384686.4 0.3846864 40 12 55CrSi 1.5 11.375 136.5 420 652128.75 0.65212875 41 9.6 SWI-200 0.5 9.552 91.7 390 341608.176 0.341608176 42 10.5 55CrSi 2.1 9.524 100 420 400008 0.400008 43 10.2 55CrSi 2 10.275 104.8 400 430728 0.430728 44 11.5 55CrSi 1.75 8.065 92.75 410 306691.7875 0.306691788 45 12.67 55CrSi 1.5 8.471 107.33 420 381860.8206 0.381860821 46 10.5 55CrSi 1.5 9.524 100 400 380960 0.38096 47 10.5 55CrSi 1.9 9.524 100 420 400008 0.400008 48 11 60Si2MnA 1.25 7.295 80.25 420 245877.975 0.245877975 49 10 60Si2MnA 0.75 5.525 55.25 400 122102.5 0.1221025 50 11 60Si2MnA 1 7.273 80 420 244372.8 0.2443728 51 10.8 60Si2MnA 0.7 7.407 80 420 248875.2 0.2488752 52 12 60Si2MnA 0.5 5.25 63 400 132300 0.1323 53 14 60Si2MnA 1 5 70 410 143500 0.1435 54 14 60Si2MnA 1 5.036 70.5 410 145565.58 0.14556558 55 10.5 60Si2MnA 0.8 6.638 69.7 400 185067.44 0.18506744 56 11 60Si2MnA 1.25 7.295 80.25 420 245877.975 0.245877975 57 11.5 60Si2MnA 0.5 9 103.5 420 391230 0.39123 |
||||||
当前位置：